Steel St52 / S355J2G3 / 1.0570

S355J2G3 steel is widely used in welded structures subjected to dynamic loads, such as bridges, vehicles, ships, pipelines, boilers, large vessels, oil tanks, heavy machinery, mining machinery and cryogenic pressure vessels.

S355J2G3 steel is widely used in welded structures subjected to dynamic loads, such as bridges, vehicles, ships, pipelines, boilers, large vessels, oil tanks, heavy machinery, mining machinery and cryogenic pressure vessels.The steel is has a wide range of application areas, such as Gear boxes, socket parts in shipbuilding, tappets, roller bodies and much more.


Chemical composition %   of   steel   S335J2G3 (1.0570):   EN 10250-2-2000
For forgings with an equivalent diameter or thickness > 100 mm the carbon content shall be agreed beetween purchaser and supplier.
CSiMnNiPSCrMoAl
max   0.22max   0.55max   1.6max   0.3max   0.035max   0.035max   0.3max   0.08min   0.02Cr+Mo+Ni < 0.48


Mechanical properties of   steel   S335J2G3 (1.0570)

Nominal thickness (mm):  to 100100 – 250250 – 500
Rm – Tensile strength (MPa) (+N)490450450


Nominal thickness(mm):  to 100100 – 250250 – 500
Re – Upper yield strength (MPa) (+N)315275265


Nominal thickness (mm):    to 100100 – 250250 – 500
A – Min. elongation at fracture (%) longitud., (+N)201818
A – Min. elongation at fracture (%) transverse, (+N)12

 

 

 

Partial part type display:

Inquiry

Upload your 3D CAD files in STL, STEP,IGES or SLDPRT format * If you have multiple files, please place them into one folder and compress the folder Please put all files into one folder and compress the folder into a ZIP or RAP file before uploading(Max 10MB). into a ZIP or RAR file. Please keep files smaller than 10MB. If attachment over 10MB, please send it to Email: info@wahimold.com directly.