TECATRON GF40 black is a 40% glass fibre reinforced PPS. Because of the high level of glass fibre reinforcement, TECATRON GF40 black demonstrates excellent rigidity and very high strength at high temperatures compared to unmodified PPS (TECATRON natural). High thermal stability, high dimensional stability, very good chemical resistance, good electrical and thermal insulation and good resistance to sterilization rounds out the property profile of this modified PPS. These material properties make glass filled PPS suitable for use in parts that are exposed to high static loads over long periods in high temperature conditions.
Colour：black，beige.
Applications
- Electrical Applications
- Housings
- Semiconductor Applications
- Structural Components
Mechanical properties
| Mechanical properties | Value | Unit | Parameter | Norm |
|---|---|---|---|---|
| Modulus of elasticity (tensile test) | 6500 | MPa | 1mm/min | DIN EN ISO 527-2 |
| Tensile strength | 83 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Tensile strength at yield | 83 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Elongation at yield (tensile test) | 2 | % | 50mm/min | DIN EN ISO 527-2 |
| Elongation at break (tensile test) | 2 | % | 50mm/min | DIN EN ISO 527-2 |
| Flexural strength | 145 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Modulus of elasticity (flexural test) | 6600 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Compression modulus | 4600 | MPa | 5mm/min, 10 N | EN ISO 604 |
| Compression strength | 21/41/105 | MPa | 1% / 2% / 5% | EN ISO 604 |
| Impact strength (Charpy) | 24 | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eU |
| Shore hardness | 91 | D | DIN EN ISO 868 |