EN AW 6063 / AlMg0.7Si(A)

Aluminium alloy 6063 is a medium strength alloy commonly referred to as an architectural alloy. It is normally used in intricate extrusions.It has a good surface finish, high corrosion resistance, is readily suited to welding and can be easily anodised. Most commonly available as T6 temper, in the T4 condition it has good formability.

6063 is used for architectural fabrication, window and door frames, pipe and tubing, and aluminium furniture

Chemical Composition

Spec: BS EN 573-3: 2009

Alloy 6063

Chemical Element % Present
Manganese (Mn) 0.0 – 0.10
Iron (Fe) 0.0 – 0.35
Magnesium (Mg) 0.45 – 0.90
Silicon (Si) 0.20 – 0.60
Zinc (Zn) 0.0 – 0.10
Titanium (Ti) 0.0 – 0.10
Chromium (Cr) 0.0 – 0.10
Copper (Cu) 0.0 – 0.10
Other (Each) 0.0 – 0.05
Others (Total) 0.0 – 0.15
Aluminium (Al) Balance

EN AW 6063 | Al Mg0.7Si(A): Heat-treated condition O

Mechanical properties

Nominal thickness mm Brinell hardness HBW Yield strength Rp0,2 MPa min./max. Tensile strength Rm MPa min./max. Elongation A50 mm % min. Elongation A % min. Bending radius 180° t min. Bending radius 90° t min.
0.5 – 6.0 65 80-140 23 0 0

EN AW 6063 | Al Mg0.7Si(A): Heat-treated condition T4

Mechanical properties

Nominal thickness mm Brinell hardness HBW Yield strength Rp0,2 MPa min./max. Tensile strength Rm MPa min./max. Elongation A50 mm % min. Elongation A % min. Bending radius 180° t min. Bending radius 90° t min.
0.5 – 6.0 40 120 20 0 0

Partial part type display:

Inquiry

Upload your 3D CAD files in STL, STEP,IGES or SLDPRT format * If you have multiple files, please place them into one folder and compress the folder Please put all files into one folder and compress the folder into a ZIP or RAP file before uploading(Max 10MB). into a ZIP or RAR file. Please keep files smaller than 10MB. If attachment over 10MB, please send it to Email: info@wahimold.com directly.