Aluminium EN AW-5083 / 3.3547 / Al-Mg4.5Mn

EN AW-5083 – CORROSION RESISTANT. EN AW-5083 belongs to the group of non-curable (naturally hard) alloys. Therefore, after homogenization, it can either be used directly or reshaped immediately. Carrying out a heat treatment to increase strength is not possible.

Der Werkstoff 3.3547 wird aufgrund seiner vielen positiven Merkmale in diversen Bereichen genutzt:

  • Apparaturen und Tanks für die chemische Industrie
  • Ausrüstungen und Tragwerke im Schiffbau
  • Automobil- und Schienenfahrzeugbau
  • Druckbehälter
  • Kippvorrichtungen (geschweißt)
  • Konstruktionen im Bau- und Straßenverkehr
  • Rohrleitungen
  • Strukturkomponenten
  • Tieftemperaturtechnik
  • Werkzeuge im Maschinenbau

Chemical Composition

 SIFeCuMnMgCrNiZnTiGaV
Min0.40.40.10.4 4.00.05 –0.150.15 – –
Max0.40.40.11.04.90.25 –0.150.15 – –
Composition in %, remainder aluminium
Material according to EN 573-3:2013
 

Mechanical Properties of Aluminium Alloy 5083

Table 2 (a). Mechanical properties for aluminium alloy 5083 Soft O/H111

BS EN 485-2:2008
Sheet
0.2 – 6.3mm Thick
PropertyValue
Proof Stress125 Min MPa
Tensile Strength275 – 350 MPa
Hardness Brinell75 HB

*Properties above are for material in the Soft O/H111 condition


Table 2 (b). Mechanical properties for aluminium alloy 5083 Soft O/H111

BS EN 485-2:2008
Plate
6.3mm to 80mm
PropertyValue
Proof Stress115 Min MPa
Tensile Strength270 – 345 MPa
Hardness Brinell75 HB

*Properties above are for material in the Soft O/H111 condition


Table 2 (c). Mechanical properties for aluminium alloy 5083 Soft O/H111

BS EN 485-2:2008
Plate
80mm to 120mm
PropertyValue
Proof Stress110 Min MPa
Tensile Strength260 Min MPa
Hardness Brinell70 HB
Elongation A12 Min %

*Properties above are for material in the Soft O/H111 condition


Table 2 (d). Mechanical properties for aluminium alloy 5083 H32

BS EN 485-2:2008
Sheet
0.2mm to 6.00mm
PropertyValue
Proof Stress215 Min MPa
Tensile Strength305 – 380 MPa
Hardness Brinell89 HB

*Properties above are for material in the H32 condition

Partial part type display:

Inquiry

Upload your 3D CAD files in STL, STEP,IGES or SLDPRT format * If you have multiple files, please place them into one folder and compress the folder Please put all files into one folder and compress the folder into a ZIP or RAP file before uploading(Max 10MB). into a ZIP or RAR file. Please keep files smaller than 10MB. If attachment over 10MB, please send it to Email: info@wahimold.com directly.