1.4122 / X39CrMo17-1

1.4122 (X39CrMo17-1) steel is a martensitic stainless steel.the 1.4122 (X39CrMo17-1) steel material is characterized by high hardness, wear resistance, and corrosion resistance. Additionally, due to its suitability for high-temperature use, it is used in equipment exposed to heat. The 1.4122 (X39CrMo17-1) material is also suitable for various mechanical processes like CNC machining, milling, and other machining operations due to its machinability.

The 1.4122 stainless steel grade is applied in the food and medical industries This 1.4122 level is used for surgical instruments such as knives, tableware, and surgical blades It is also used for plastic molds that require wear resistance, such as slides, injection nozzles, and extrusion screws,also be used to manufacture tools for cutting wood or metal, such as carving and cutting tools, turning tools, and milling cutters.

Chemical composition %   of   steel   X39CrMo17-1 (1.4122):   EN 10088-2-2005

C Si Mn Ni P S Cr Mo
0.33 – 0.45 max   1 max   1.5 max   1 max   0.04 max   0.015 15.5 – 17.5 0.8 – 1.3

Mechanical properties of   steel   X39CrMo17-1 (1.4122)

Rm – Tensile strength (MPa) (+A)900
Rm – Tensile strength (MPa) (+QT750)750-950


Rp0.2 0.2% proof strength (MPa) +QT750550


KV – Impact energy (J) longitud., (+QT)+20°
14-20


A – Min. elongation at fracture (%) (+A)12


  Brinell hardness   (HB):   (+A)280


Partial part type display:

Inquiry

Upload your 3D CAD files in STL, STEP,IGES or SLDPRT format * If you have multiple files, please place them into one folder and compress the folder Please put all files into one folder and compress the folder into a ZIP or RAP file before uploading(Max 10MB). into a ZIP or RAR file. Please keep files smaller than 10MB. If attachment over 10MB, please send it to Email: info@wahimold.com directly.