1.4016 / AISI 430 / X6Cr17

Stainless steel type 1.4016 is also commonly known as grade 430.Type 430 stainless steel combines good corrosion resistance with good formability and ductility. It is a ferritic, non-hardenable plain chromium stainless steel with excellent finish quality.Grade 430 also has excellent resistance to nitric attack, which makes it well suited to use in chemical applications. The most popular applications for 430 are in domestic appliances and decorative trim.

Applications

  • Low cost sinks
  • Decorative trim
  • White & brown Goods (washing machines, dishwashers, cookers)
  • Refrigerators
  • Stove element supports
  • Scientific apparatus
  • Fasteners
  • Flue linings
  • Automotive trim
  • Hinges

Chemical Composition

1.4016 Steel

Chemical Element% Present
Carbon (C)0.0 – 0.08
Chromium (Cr)16.00 – 18.00
Manganese (Mn)0.0 – 1.00
Silicon (Si)0.0 – 1.00
Phosphorous (P)0.0 – 0.04
Sulphur (S)0.0 – 0.02
Iron (Fe)

Balance

Mechanical Property

Sheet – Up to 8mm Thick

Mechanical PropertyValue
Proof Stress260 Min MPa
Tensile Strength450 – 600 MPa
Elongation A50 mm20 Min %

Spec: EN 10088-2:2005

Plate – Over 8mm to 13.5mm / Thick

Mechanical PropertyValue
Proof Stress240 Min MPa
Tensile Strength450 – 600 MPa
Elongation A50 mm18 Min %

Spec: EN 10088-2:2005

Plate – Over 13.5mm to 25mm Thick

Mechanical PropertyValue
Proof Stress240 Min MPa
Tensile Strength430 – 630 MPa
Elongation A50 mm20 Min %

Partial part type display:

Inquiry

Upload your 3D CAD files in STL, STEP,IGES or SLDPRT format * If you have multiple files, please place them into one folder and compress the folder Please put all files into one folder and compress the folder into a ZIP or RAP file before uploading(Max 10MB). into a ZIP or RAR file. Please keep files smaller than 10MB. If attachment over 10MB, please send it to Email: info@wahimold.com directly.