One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Composition
Element | Weight % |
C | 0.13 (max) |
Mn | 0.70-1.00 |
P | 0.07-0.12 |
S | 0.16-0.23 |
Mechanical Properties
Properties | Conditions | ||
T (°C) | Treatment | ||
Density (×1000 kg/m3) | 7.7–8.03 | 25 | |
Poisson’s Ratio | 0.27-0.30 | 25 | |
Elastic Modulus (GPa) | 190–210 | 25 | |
Tensile Strength (Mpa) | 540 | 25 | cold drawn (round bar (19-38 mm)) |
Yield Strength (Mpa) | 415 | ||
Elongation (%) | 10 | ||
Reduction in Area (%) | 35 | ||
Hardness (HB) | 167 | 25 | cold drawn (round bar (19-38 mm)) |