C35 steel is a medium carbon, medium tensile steel supplied as-forged or normalized condition.This steel shows excellent forgeability, reasonable strength, toughness and wear resistance. C35 is easily welded with the correct procedure.Due to the carbon content preheating and postheating are required.It has good Machinability after full annealing.Wide range of mechanical properties can be attained by quenching and tempering,as quenched hardness should be approximately 45 HRC.
C35 steel is widely used in the manufacture of various forgings and hot-pressed parts, cold-drawn and upsetting steels, seamless steel pipes, parts in machinery manufacturing, such as crankshafts, rotating shafts, shaft pins, levers, connecting rods, beams, sleeves, wheels Rings, washers, screws, nuts, etc.
C35 Steel Chemical Composition
| Grade | C | Si | Mn | P | S |
| C35/1.0501 | 0.32-0.39 | ≤ 0.4 | 0.50-0.80 | ≤ 0.045 | ≤ 0.045 |
C35 Steel Mechanical Property
| Diameter d mm | ≤ 16 | 16-40 | 40-100 |
| Thickness t mm | < 8 | 8-20 | 20-60 |
| Yield Strength Mpa | ≥430 | ≥380 | ≥320 |
| Tensile Strength Mpa | 630-780 | 600-750 | 550-700 |
| Elongation, % | ≥17 | ≥19 | ≥20 |
| Reduction of area ,% | ≥40 | ≥45 | ≥50 |